Abstract Alumina (Al2O3) suffers from low fracture toughness and low bending strength which restrict its application in the industry for some advanced components. The incorporation of submicron SiC into Al2O3 matrix improves mechanical properties of the matrix. However, the high cost of SiC has delayed the industrial interest of synthesizing Al2O3-SiC composites. Rice husk, an agricultural waste material, is a potential source of low-cost SiC. Therefore, this study presents a simple approach to synthesizing SiC from locally sourced rice husk and using it to reinforce alumina. Rice husk was pyrolysed in a tube furnace under argon atmosphere at different temperatures (1000 °C – 1500 °C) and reaction times (60 – 120 min). Furthermore, Alumina powder was admixed with 5 – 20 vol% SiC derived from rice husk, and then sintered at temperatures between 1300 °C – 1600 °C by spark plasma sintering. Maximum yield of SiC was obtained from rice husk at 1500 °C and 120 min. Materials with theoretical densities higher than 95% were achieved for the sintered composites. The hardness of sintered composites reached a maximum of 20.2±1.4 GPa, while a maximum of 4.7±.7 MPa.m0.5 was obtained for the fracture toughness.

This paper reports on the effect of scanning speed on the laser deposited Cu on titanium alloy substrate. The experiments were conducted by varying the scanning speed from 0.3 m/min to 1.2 m/min while the laser power, the powder feed rate and the gas flow rate were kept constant. The laser deposited Cu were characterized through the evolving microstructure and surface roughness. Dendrites and acicular were much pronounced in the clad area; found to decrease as the scanning speed increases due to the laser interaction time and the cooling rate. These however, influenced the irregularities in the peaks and valleys of the surface texture. The arithmetic mean deviation, Ra were measured and abridged from 6.70 µm to 1.41 µm as the scanning speed was increased from samples DC1 to DC4. The motivation for this work is to improve the surface performance of Ti6Al4V alloy when exposed and attacked by marine microfouling organisms.

Surface engineering applications have brought the titanium and its alloys into the limelight in the manufacturing industries such as the aerospace, automobile, marine, chemical processing industry, nuclear power and biomedical. Despite the growths experienced in the use of this material, it is plagued with poor wear behaviour, especially when in contact with other materials during application. In this research work, the reinforcement of titanium alloy (Ti6Al4V) and boron carbide (B4C) ceramic powders was employed to form the Ti6Al4V+B4C composites. The effect of laser power on the micrograph, microhardness, surface roughness and wear has been investigated. The micrographic evaluation, the geometrical analyses and the effect of laser power on the width and height of deposit, aspect ratio and dilution rate were also evaluated. The highest aspect ratio of 5.31 and dilution rate of 63.81 % was observed in sample MB5 deposited with a laser power of 2400 W. The dry sliding friction and wear conducted using a 10 mm diameter tungsten carbide ball and a normal load of 25 N revealed that sample MB2 produced at a laser power of 1800 W has the lowest wear depth and wear width of 74.6 µm and 1080.77 µm. From the lowest COF attributed by sample MB5, it can be inferred that coefficient of friction does not determine the wear loss due to the sticking of some wear debris to the wear track during sliding action. Thus, other wearing factors are also considered for the wear loss evaluation. However, this composite can be used for the repair of the worm part of a rotating shaft and turbine blades.